| EVA 7130 技术指数 |
| 基本物性 |
单位 |
测试方法 |
7130 |
| 熔融指数MI2.16 |
g/10min |
ASTM D1238 |
0.9 |
| 密度 |
g/cm3 |
ASTM D1505 |
0.930 |
| VA含量 |
％ |
|
9 |
| 热性质 |
| 熔点 |
℃ |
DSC |
93 |
| 脆化温度 |
℃ |
ASTM D746 |
<-80 |
| 软化点 |
℃ |
ASTM D1525 |
80 |
| 机械性质 |
| 降伏点强度 |
kg/cm2 |
ASTM D638 |
60 |
| 断裂点强度 |
kg/cm2 |
ASTM D638 |
180 |
| 断裂点伸长率 |
％ |
ASTM D638 |
650 |
| 弯曲模量 |
kg/cm2 |
ASTM D790 |
700 |
| 硬度 |
shord A |
ASTM D2240 |
95 |
| 硬度 |
shord D |
ASTM D2240 |
45 |
| 薄膜机械性质 |
| 降伏点强度 |
kg/cm2 |
ASTM D882B MD/TD |
50/40 |
| 断裂点强度 |
kg/cm2 |
ASTM D882B MD/TD |
300/280 |
| 断裂点伸长率 |
％ |
ASTM D882B MD/TD |
400/550 |
| 1%伸长弹性系数 |
kg/cm2 |
ASTM D882B MD/TD |
350/400 |
| 抗撕裂性 |
g/25μm |
ASTM D882B MD/TD |
10/24 |
| 落球冲击强度 |
g |
ASTM D1709 |
>0.5 |
| 光学性质 |
| 浊度 |
％ |
ASTM D1003 |
5 |
| 光泽度45° |
％ |
ASTM D2457 |
80 |
| 建议薄膜厚度 |
μ |
|
30-150 |
| 添加剂 |
| 滑剂 |
等级 |
|
|
| 抗粘剂 |
等级 |
|
|
| 特性 |
韧性佳 不含BHT |
| 用途 |
温室膜 农业膜 医药用途 |
|
|
|